Maraging Steel C300 Wire
Maraging Steel 300/ C300 (AMS 6514)
Maraging 300 is an age hardenable (maraging) iron nickel stainless steel. Maraging 300 has exceptional strength, toughness and is resistant to crack propagation. Maraging 300 is used for tooling, transmission shafts, autosport components and light aircraft landing gear.
|
Maraging Steel C200 C250 C300 C350(18Ni) special stainless steel Chemical Composition Limits |
|||||||||||||
|
C |
S |
P |
|||||||||||
|
C200 |
17.0-19.0 |
8.0-9.0 |
0.10 |
0.10 |
0.03 |
0.05-0.15 |
3.0-3.5 |
0.01 |
0.01 |
0.15-0.25 |
0.50 |
0.50 |
|
|
C250 |
17.0-19.0 |
7.0-8.5 |
0.10 |
0.10 |
0.03 |
0.05-0.15 |
4.6-5.2 |
0.01 |
0.01 |
0.30-0.50 |
0.50 |
0.50 |
|
|
C300 |
18.0-19.0 |
8.5-9.5 |
0.10 |
0.10 |
0.03 |
0.05-0.15 |
4.6-5.2 |
0.01 |
0.01 |
0.50-0.80 |
0.50 |
0.50 |
|
|
C350 |
18.0-19.0 |
11.5-12.5 |
0.10 |
0.10 |
0.03 |
0.05-0.15 |
4.6-5.2 |
0.01 |
0.01 |
1.30-1.60 |
0.50 |
0.50 |
|
|
|
|
Elongation in 4D percent |
|
||||
|
Maraging C200 |
After Maraging heat treatment 900ºF |
1379 |
200 |
1200 |
190 |
8 |
48HRC |
|
Maraging C250 |
After Maraging heat treatment 900ºF |
1758 |
255 |
1724 |
250 |
6 |
48HRC |
|
Maraging C300 |
After Maraging heat treatment 900ºF |
2035 |
298 |
1915 |
280 |
5 |
52HRC |
|
Maraging C350 |
After Maraging heat treatment 900ºF |
2394 |
350 |
2257 |
330 |
2.8 |
56HRC |
| 0.2 percent Yield Strength ksi | Elongation in 4D( percent ) | ||||
| Maraging 300, Solution Annealed 1500 degree F (816 degree ), 1hr, AC | 120 | 150 | 16 | 70 | 30 |
| Solution Annealed Plus Aged 900 degree F (482 degree ), 3 hrs AC | 280 | 290 | 8 | 40 | 52 |